LEGHE Ney per CERAMICA
Cat LEGA COMPOSIZIONE in % (=<2%) Intervallo fusione Temperatura Colata Peso Specifico Durezza Vichers Coeff (1) espans. Termica Carico di rottura psi-Mpa Limite (2) di elasticit psi-Mpa Allung. Temperatura preriscald. Nobilt
Au Pt Pd Ag Cu In Zn Sn Ga Ir altri < 2% dwt / in (3) g/cm (3)
YELLOW GOLD BIONEY 90,0 7,25   1,0   X X       Re-Fe 1890-2000F 1030-1095C 2175F 1190C 199 18,9 180+ 14,8 79.800+ 550+ 69.600+ 480+ 9+ 1300F 700C HN
SUPER BIONEY 82,4 15,0         X       Re-Fe 1905-2050F 1040-1120C 2210F 1210C 198 18,8 220+ 14,2 87.000+ 600+ 74.000+ 510+ 9+ 1300F 700C HN
IMAGE 2 84,5 6,9 5,0 1,0   X X       Re-Fe 1994-2183F 1090-1195C 2354F 1290C 190 18,0 230+ 14,5 111.700+ 770+ 97.300+ 671+ 7+ 1300F 700C HN
ECXEL 82,0           X       Re-Fe 1905-2050F 1040-1120C 2210F 1210C 198 18,8 220+ 14,2 97.900+ 650+ 87.000+ 600+ 6+ 1300F 700C HN
WHITE GOLD SMG-3 81,0 6,0 11,0         X     Re-Fe 2120-2320F 1160-1270C 2430F 1335C 183 17,4 240 13,9 112.000 770 101.000 700 5 1300F 700C HN
SMG-PF 78,0 20,0       X X     X   1976-2320F 1080-1315C 2580F 1415C 200 19,0 215+ 13,9 95.700+ 660+ 87.000 600 5+ 1300F 700C HN
SMG-CF 67,4   22,0 4,9   X     X   Ru 2180-2310F 1195-1265C 2530F 1390C 164 15,6 220 14,2 103.000 710 82.000 565 7 1470F 800C HN
ECLIPSE 52,0   37,5     3,0 4,0 3,0     Re 2120-2310F 1195-1265C 2498F 1370C 145 13,8 254 13,8 117.000 805 83.400 575 23 1300F 700F HN
ASPIRE 52,0   25,6 17,0   X 3,0 X   X Ru 2140-2280F 1170-1250C 2500F 1370C 150 14,2 210 14,7 125.000 860 52.000 360 11 1470F 800C HN
ENCORE 48,0   40,0     4,0 3,0       Re 2113-2330F 1156-1275C 2525F 1385C 141 3,4 250 14,1 115.000 793 85.900 592 20 1300F 700F HN
VERITAS 40,0   45,0 50,0   2,5 2,5 5,0     Re 2210-2390F 1210-1310C 2525F 1385C 137 13,0 232 14,1 107.000 740 61.600 425 40 1300F 700C HN
HIGH PALLAD. OVATION 30,0   69,8 9,7   2,0 5,0 9,8 X   Ru 2110-2350F 1155-1285C 2530F 1385C 113 10,7 255 14,0 150.000 1035 92.800 640 16 1400F 760C N
OPTION 2,0   78,8   10,0       9,0 X B 2012-2174F 1100-1190C 2354F 1290C 112 10,6 425 14,3 167.000 1150 130.500 900 23 1300F 700C N
PALLADIUM SILVER LUNAR     60,0 29,5   X X 60,0   X   2160-2350F 1180-1290C 2500F 1370C 116 11,0 244 14,7 102.000 700 64.000 440 35 1500F 815C N
PDPRO     53,5 37,5   3,0 X 8,4   X   2175-2310F 1190-1265C 2480F 1360C 114 10,8 250 15,1 95.700 660 67.500 465 15 1400F 760C N
ACCLAIM LITE     50,0 40,0   9,0     X   Re-Ru 2100-2310F 1150-1265C 2440F 1340C 113 10,7 300 15,1 120.400 830 92.100 635 10 1300F 700C N
LOW FUSING MULTI-PF 69,0 10,0   13,5 5,5   2,0     X   1720-1890F 940-1030C 2060F 1125C 169 16,6 230 16,6 102.000 700 77.000 530 18 1300F 700C HN
NEY-ORO 66CF 60,0   6,0 30,0   2,0 2,0         1760-1975F 960-1080C 2140F 1170C 150 17,1 240 17,1 92.000 635 82.000 565 8 1250F 650C HN
SONOMA     37,0 56,0     X X   X   1922-2066F 1050-1130C 2280F 1250C 115 16,5 180 16,5 81.000 560 47.800 330 10 1470F 800C N

clicca sul nome della lega per visonare le modalità d'uso e le saldature consigliate
NEY, ACCLAIM LITE, BIONEY, LUNAR, NEY-ORO, OPTION, OVATION e SMG sono marchi registrati dalla NEY
  1 = X10-6/° C@ 500°C
LEGENDA: 2 = 0.2 % Offset
  + =Temprata o dopo cottura ceramica
  HN = high Noble
  N = Noble