LEGHE Ney per RESINA
Cat LEGA TIPO COMPOSIZIONE in % (=<2%) Intervallo fusione Temper. Colata Peso Specifico Durezza Vichers   Carico di rottura psi-Mpa Limite (2) di elasticit psi-Mpa Allung. Temperatura preriscald. Nobilt
Au Pt Pd Ag Cu In Zn Sn Ga Ir altri < 2% dwt / in (3) g/cm (3)
PREMIUM YELLOW NEY-ORO A-1 II 77,5   2,0 12,5 7,3   X         1702-1774F 928-968C 1940F 1060C 169 16,0 125   62.200 429 33.400 230 48 1200F 650C HN
NEY-ORO PF-CB III 80,0 1,0   9,0 9,0   X     X   1625-1715F 885-935C 1875F 1025C 171 16,2 126   62.000 430 39.900 275 45 1200F 650C HN
NEY-ORO B-2 III 74,0   4,0 11,5 10,0   X         1679-1771 F 915-966C 1940F 1060C 159 15,1 185+   78.000+ 538+ 46.600+ 321+ 39+ 1200F 650C HN
NEY-ORO G-3 III 68,5 2,5 4,0 12,0 11,0   2,0         1663-1740F 906-949C 1913F 1045C 154 14,6 282+   129.000+ 889+ 100.000+ 690+ 13+ 1200F 650C HN
YELLOW HIGH NOBLE NEY-ORO # 5 IV 63,0   5,0 19,0 12,0   X         1635-1733F 890-945C 1895F 1035C 152 14,4 260+   116.000+ 800+ 99.000+ 685+ 15+ 1200F 650C HN
NEY-ORO CB IV 59,0   4,0 22,5 13,5   X     X   1580-1661F 860-905C 1823F 995C 147 13,9 275+   129.000+ 889+ 115.300+ 795+ 11+ 1200F 650C HN
NEY-ORO 60 IV 56,0   4,0 19,9 1,7   3,0     X   1540-1589F 835-865C 1751F 955C 141 13,4 265+   130.000+ 896+ 114.600+ 790+ 8+ 1200F 650C HN
YELLOW NOBLE MAJORITY III 50,0   4,5 10,0 31,0   4,0     X   1540-1630F 835-885C 1814F 990C 132 12,5 220+   86.200+ 708+ 76.300+ 526+ 7+ 1200F 650C N
MIRACAST III 40,9 1,0 4,0 9,0 38,0   7,0     X   1544-1700F 840-925C 1877F 1025C 124 11,8 158+   84.400+ 582+ 49.300+ 340+ 39+ 1200F 650C N
MAGNA III 45,0   6,0 39,0 8,5   X         1625-1787F 885-975C 1950F 1070C 134 12,7 240+   90.000+ 620+ 78.000+ 522+ 11+ 1200F 650C N
ECONOM. NEY 76 III     25,0 59,0 14,0   2,0         1650-1800F 900-980C 1976F 1080C 110 10,5 235+   108.900+ 751+ 95.700+ 660+ 9+ 1200F 650C N

clicca sul nome della lega per visonare le modalità d'uso e le saldature consigliate
NEY, NEY-ORO, e MAJORITY sono marchi registrati dalla Ney
   
2 = 0.2 % Offset
LEGENDA: + =Temprata o dopo cottura ceramica
  HN = high Noble
  N = Noble

Torna ai prodotti